Two Parts Pad Printing Silicone Rubber for Trademarks and Irregular Pattern

• Customization: Available
• Material: Organic Silicone
• Application: Industrial
• Model NO.: INI-9 Series
• Certification: ISO, FDA, REACH, RoHS
• Use: Pad Printing
• Appearance: Liquid
• Hardness: 33 Shore a
• Mix Ratio: 9:1
• Viscosity: 12000 Cps
• Elongation: 450%
• Shelf Life: 12 Months
• Package: 25kg/200kg
• Lead Time: 3-5 Days After Payment Receiving.
• Certificates: FDA, MSDS, Reach, RoHS, ISO
• Color: Reddish Brown
• Operate Time: 30-50 Minutes
• Curing Time: 3-5 Hours
• Curing Temperature: 25c
• Shrinkage Rate: Less Than 0.1%
• Transport Package: 25kg/200kg
• Trademark: INIBABA
• Origin: Shenzhen, China
• HS Code: 39100000
• Production Capacity: 800 Tons Per Year
• Package Size: 90.00cm * 90.00cm * 90.00cm
• Package Gross Weight: 20.000kg
• Lead Time: 3 days (1 - 200 kg) ; 5 days (201 - 500 kg) ; 7 days (501 - 1000 kg) ; To be negotiated ( > 1000 kg)

Product Description

 

Pad Printing Silicone
INI-933

Description  
Two-component silicone, platinum-curing, flowable, vulcanizes at room temperature.
Can be used for a long time in the temperature range of - 65 ° C - 200 ° C and keep its soft and elastic properties.


Application
Suitable for making printing pads, tampo pads for transfer patterns and contents to the porcelain /ceramics, plastic, electroplated products, toys, tableware and so on.




Features & Advantages

• The liquid silicone very delicate without any impurities or particles.
• Excellent resilience & elasticity
• Durable, the printing times can more than 50000 times without sign of tearing or wearing on pads for some items.
• Good oil absorption effect
• The pattern is printed with great clarity and completeness.
• Keep good quality even though 200%-300% silicone oil added

• Low shrinkage
• No bubbles
• Adjustable with excellent antistatic performance

Typical properties INI-933

Properties Index		Test Report
Before Curing	Appearance	Fluid
	Viscosity(cps)	9000±2000 (Adjustable)
Operating	Mixing Ratio (By weight)	9 :1
	Operating Time(25ºC  /min)	30~40  (Adjustable)
	Curing time (hr, basically cured)	3~5  (Adjustable)
	Curing time (hr, perfectly cured)	12
After Curing	Hardness (shore A)	34±3
	Tear strength (kN/m)	23±2
	Tensile strength (Mpa)	5.4±0.4
	Shrinkage (%)	≤0.1
	Elongation (%)	360~410
	Density (g/cm)	1.09

 

Operation instructions

1. Mix part A and pars B evenly with 100:3 mixing ratio.

Notes: 1) Weigh the two parts exactly by electronic weight. For example, the operation time will be shorten after adding too much catalyst.

 

           2)Mix part A and part B evenly. Otherwise the silicon rubber will be partly solidified which will make the finished molds meet a short life and waste silicon rubber.

 

         

       2.Vacuum pumping

 

Notes: 1) This step is not have to have, but it is best if there is one. It will discharge all air in the mixture successfully, so as to ensure that there

will be no bubbles in the finished mold.

 

          2) This step is less than 10 minutes. Otherwise, it Will cause cross-linking reaction, and no more further steps will be available.

 

 

     3.Pouring casting or Brush molding

 

Notes:1) For simple pattern products we suggest use pouring operation way, which will be very easy to operate and demould. Pourable silicone require low viscosity which will be easy to flow smoothly and easy to de-air.

 

           2)For delicate pattern products we suggest use brushing operation way, which can copy the pattern exactly. Brushable silicone require high viscosity which won't be easy to flow away and easy to brush.      

 

           3)We suggest to set the mold for another 12 hours after demould before put it into large production.




Package details:1kg/5kg/20kg/25kg/200kg